Effect of epigallocatechin-3-gallate and thermal cycling on the bond strength of resin cements to the root dentin.

This study evaluated the effect of epigallocatechin-3-gallate (EGCG) solution and thermal cycling on the bond strength (BS) of fiber posts to the root dentin using two different resin cements (conventional or self-adhesive). One hundred and forty-four bovine roots were endodontically treated. After post space preparation, specimens were randomly divided into six groups (n = 24) according to dentin pretreatment [distilled water, 0.05% EGCG solution or 2% chlorhexidine (CHX) solution] and resin luting agent used for fiber post cementation (RelyX ARC or RelyX U200-3 M ESPE). Then, the samples were separated into two subgroups (n = 12): storage in distilled water at 37 °C for 24 h and thermal cycling (5 °C/55 °C, dwell time 30 s-12,000 cycles) during 6 months. After that, the specimens were subjected to the pull-out BS test (Universal Testing Machine-0.5 mm/min) and the failures pattern was analyzed in a stereomicroscope. According to the BS results (three-way ANOVA, Tukey's test, α = 0.05), the highest values were reported in the group EGCG + RelyX U200, showing significant statistical differences compared to all the other experimental groups. For Control and CHX groups BS values, there was no significant difference (p > .05) between the resin cements. For conventional resin cement, there was no significant difference among treatment solutions (p > .05). The thermal cycling did not influence the BS results (p > .05). As reported by the failure mode analysis, adhesive failure was predominant in all groups. EGCG solution improved the bond strength of self-adhesive resin cement to root dentin.

Influence of Sealer and Light-Curing Units on Push-Out Bond Strength Of Composite Resin to Weakened Roots.

The aim of this study was to assess the influence of sealer and light-curing unit on regional bond strength of resin composite to the weakened roots. Ninety roots of incisors were experimentally weakened, subjected to biomechanical preparation and filled with either Endofill, AH Plus or MTA Fillapex The roots were desobturated e reinforced with resin composite and fiber post light-activated with one of the light sources: halogen at 600 mW/ cm2 (QTH-600), LED at 800 mW/ cm2 (LED-800) and LED at 1500 mW/ cm2 (LED-1500). The roots were sectioned in slices from cervical, middle and apical root-reinforcement regions and analyzed by push out test, scanning electron microscopy (SEM) and confocal laser scanning microscopy (CLSM). Bond strength data were analyzed using three-way ANOVA and Tukey´s test (α=0.05). Specimens filled with AH Plus had higher bond strength, followed by MTA Fillapex and Endofill (p<0.05). For light-curing unit, LED-1500 presented superior bond strength than LED-800, which was higher than QTH-600 (p<0.05). The cervical region had the greatest mean values (p<0.05) while apical part showed the lowest bond strength (p<0.05). CLMS revealed remaining filling material in the dentinal tubules for all groups. The eugenol-containing sealer (Endofill) compromised the push-out bond strength of composite resin to the root dentin. Bond strength was favored in the cervical region, and when LED-1500 was used.

1064-nm Nd:YAG and 980-nm Diode Laser EDTA Agitation on the Retention of an Epoxy-Based Sealer to Root Dentin.

Root canal irrigants are used to minimize the negative effects of smear layer on endodontic sealer retention. The aim of this study was to evaluate the efficacy of agitation of 17% ethylenediaminetetraacetic acid (EDTA) with ultrasonic, 1064-nm Nd:YAG and 980-nm diode laser on the retention of an epoxy-based sealer to the root canal walls. Forty single-rooted bovine teeth were instrumented with ProTaper rotary system and divided into four groups according to the final irrigation protocol (n = 10): (1) 17% EDTA (control); (2) 17% EDTA with 50-s ultrasonic agitation; (3) 17% EDTA with 50-s diode laser (2-W) agitation; and (4) 17% EDTA with 50-s Nd:YAG (1.5-W) laser agitation. After endodontic filling with gutta-percha F5 master cone and Sealer 26, the roots were sectioned at the cervical, middle, and apical root thirds to obtain 1.5-mm slices. Push-out tests were performed using a universal testing machine at a 1 mm/min crosshead speed. Data were analyzed using two-way ANOVA and Tukey's tests (α=0.05). Apical root thirds had significant higher retention values than cervical and middle thirds (p < 0.05). EDTA with 1064-nm Nd:YAG or 980-nm diode laser presented the highest retention values and was significantly different from EDTA with ultrasonic agitation and EDTA only (p < 0.05). Adhesive failures were predominant to EDTA only group. Mixed failures were predominant to all agitation groups. 1064-nm Nd:YAG and 980-nm diode laser EDTA agitation enhanced the retention of the epoxy-based sealer to the root canal walls compared with that due to EDTA only or EDTA with ultrasonic agitation.

Influence of Sealer and Light-Curing Units on Push-Out Bond Strength Of Composite Resin to Weakened Roots

Abstract The aim of this study was to assess the influence of sealer and light-curing unit on regional bond strength of resin composite to the weakened roots. Ninety roots of incisors were experimentally weakened, subjected to biomechanical preparation and filled with either Endofill, AH Plus or MTA Fillapex The roots were desobturated e reinforced with resin composite and fiber post light-activated with one of the light sources: halogen at 600 mW/ cm2 (QTH-600), LED at 800 mW/ cm2 (LED-800) and LED at 1500 mW/ cm2 (LED-1500). The roots were sectioned in slices from cervical, middle and apical root-reinforcement regions and analyzed by push out test, scanning electron microscopy (SEM) and confocal laser scanning microscopy (CLSM). Bond strength data were analyzed using three-way ANOVA and Tukey´s test (α=0.05). Specimens filled with AH Plus had higher bond strength, followed by MTA Fillapex and Endofill (p<0.05). For light-curing unit, LED-1500 presented superior bond strength than LED-800, which was higher than QTH-600 (p<0.05). The cervical region had the greatest mean values (p<0.05) while apical part showed the lowest bond strength (p<0.05). CLMS revealed remaining filling material in the dentinal tubules for all groups. The eugenol-containing sealer (Endofill) compromised the push-out bond strength of composite resin to the root dentin. Bond strength was favored in the cervical region, and when LED-1500 was used.

Resumo O objetivo neste estudo foi avaliar a influência do cimento endodôntico e da fonte de luz fotoativadora na resistência de união (RU) regional da resina composta às raízes fragilizadas. Noventa raízes de incisivos foram experimentalmente fragilizados, submetidos ao preparo biomecânico e obturadas com Endofill, AH Plus ou MTA Fillapex. Os canais foram desobturados e reforçados com pinos de fibra de vidro e resina composta fotoativada com uma das fontes de luz: halógena a 600 mW/cm2 (QTH-600), diodo emissor de luz a 800 mW/cm2 (LED-800) e LED a 1500 mW/cm2 (LED-1500). As raízes foram seccionadas em slices provenientes dos terços cervical, médio e apical das regiões da raiz reforçada e analisadas por meio do teste de push out, microscopia eletrônica de varredura (MEV) e microscopia confocal de varredura a laser (MCVL). Os dados de resistência de união foram analisados por ANOVA a três critérios e teste de Tukey (α=0,05). Os espécimes obturados com AH Plus apresentaram maior resistência de união, seguido do MTA Fillapex e do Endofill (p<0,05). Para fonte de luz fotoativadora, LED-1500 apresentou resistência de união superior ao LED-800 que foi maior que QTH-600 (p<0,05). A região cervical obteve as maiores médias (p<0,05), enquanto que a região apical apresentou a menor resistência de união (p<0,05). MCVL revelou remanescente de material endodôntico nos túbulos dentinários para todos os grupos. O cimento contendo eugenol (Endofill) comprometeu a resistência de união da resina composta à dentina radicular. A resistência de união foi favorecida na região cervical, e quando o LED-1500 foi empregado.

1064-nm Nd: YAG and 980-nm Diode Laser EDTA Agitation on the Retention of an Epoxy-Based Sealer to Root Dentin

Abstract Root canal irrigants are used to minimize the negative effects of smear layer on endodontic sealer retention. The aim of this study was to evaluate the efficacy of agitation of 17% ethylenediaminetetraacetic acid (EDTA) with ultrasonic, 1064-nm Nd:YAG and 980-nm diode laser on the retention of an epoxy-based sealer to the root canal walls. Forty single-rooted bovine teeth were instrumented with ProTaper rotary system and divided into four groups according to the final irrigation protocol (n = 10): (1) 17% EDTA (control); (2) 17% EDTA with 50-s ultrasonic agitation; (3) 17% EDTA with 50-s diode laser (2-W) agitation; and (4) 17% EDTA with 50-s Nd:YAG (1.5-W) laser agitation. After endodontic filling with gutta-percha F5 master cone and Sealer 26, the roots were sectioned at the cervical, middle, and apical root thirds to obtain 1.5-mm slices. Push-out tests were performed using a universal testing machine at a 1 mm/min crosshead speed. Data were analyzed using two-way ANOVA and Tukey's tests (α=0.05). Apical root thirds had significant higher retention values than cervical and middle thirds (p < 0.05). EDTA with 1064-nm Nd:YAG or 980-nm diode laser presented the highest retention values and was significantly different from EDTA with ultrasonic agitation and EDTA only (p < 0.05). Adhesive failures were predominant to EDTA only group. Mixed failures were predominant to all agitation groups. 1064-nm Nd:YAG and 980-nm diode laser EDTA agitation enhanced the retention of the epoxy-based sealer to the root canal walls compared with that due to EDTA only or EDTA with ultrasonic agitation.

Resumo Irrigantes para canais radiculares são usados para minimizar os efeitos negativos da camada de smear na retenção do cimento obturador. O objetivo deste estudo foi avaliar a eficácia da agitação do ácido etilenodiaminotetracético a 17% (EDTA) com ultrassom, Nd:YAG 1064-nm e laser diodo 980-nm na retenção de um cimento obturador à base de resina epóxica nas paredes do canal radicular. Quarenta dentes bovinos unirradiculares foram instrumentados com o sistema rotatório ProTaper e divididos em quatro grupos de acordo com o protocolo de irrigação final (n = 10): (1) EDTA 17% (controle); (2) EDTA 17% com agitação ultrassônica por 50-s; (3) EDTA 17% com agitação com laser diodo (2-W) por 50-s; e (4) EDTA 17% com agitação com laser Nd:YAG (1,5-W) por 50-s. Após obturação endodôntica com cone principal F5 e cimento Sealer 26, as raízes foram seccionadas nos terços radiculares cervical, médio e apical para obtenção de slices de 1,5-mm. Testes de push-out foram realizados utilizando uma máquina universal de ensaios com velocidade de carga de 1 mm/min. Os dados foram analisados utilizando os testes two-way ANOVA e Tukey's (α=0,05). Os terços radiculares apicais tiveram força de adesão significantemente maior que os terços cervical e médio (p<0,05). EDTA com Nd:YAG 1064-nm ou laser diodo 980-nm apresentaram os maiores valores de força de adesão e foram significantemente diferentes do EDTA com agitação ultrassônica e EDTA apenas (p < 0,05). Falhas adesivas foram predominantes apenas no grupo EDTA. Falhas mistas foram predominantes em todos os grupos de agitação. A agitação do EDTA com Nd:YAG 1064-nm e laser diodo 980-nm aumentou a força de adesão do cimento à base de resina epóxica às paredes do canal radicular comparado com a obtida com EDTA apenas ou EDTA com agitação ultrassônica.

Bonding Effectiveness of Universal Adhesive to Intracoronal Bleached Dentin Treated with Sodium Ascorbate

Abstract This study evaluated the effect of restorative protocol with sodium ascorbate on the shear bond strength (SBS) of a universal adhesive to intracoronal bleached dentin. One hundred-and-twenty bovine dentin fragments were randomly divided into 12 groups (n=10), according to the bleaching procedure (unbleached and bleached) and restorative protocol (no treatment, 10% sodium ascorbate -10SA, 35% sodium ascorbate -35SA and two-step etch-and-rinse -ER or one-step self-etch -SE Scotchbond universal adhesive approaches). Four whitening sessions were performed using 35% hydrogen peroxide. The samples from control groups were kept in relative humidity at 37 °C. Immediately after bleaching procedures, the assigned antioxidant solution was applied on dentin and restorative procedures were performed following either the ER or the SE approach. After 24 h, the specimens were subjected to SBS test. Data (MPa) were analyzed by ANOVA and Tukey's test (?=0.05). Lower SBS values were found for bleached specimens (8.54 MPa) compared with those unbleached (12.13 MPa) (p<0.05). The bond strength of the sodium ascorbate-treated groups was higher than those untreated, regardless of the strategy employed (p<0.05). Groups restored without sodium ascorbate showed lower bond strength values for both ER (8.32 MPa) and SE (8.28 MPa) adhesive strategies. The group treated with 10SA submitted to ER approach (10.14 MPa) was similar to untreated groups (p>0.05). It may be concluded that bond strength of composite resin to intracoronal dentin was affected by restorative protocol and reduced by bleaching.

Resumo Este estudo avaliou o efeito do protocolo restaurador empregando ascorbato de sódio na resistência ao cisalhamento do adesivo universal à dentina intracoronária clareada. Cento e vinte fragmentos de dentina bovina foram aleatoriamente divididos em doze grupos (n=10), de acordo com o procedimento clareador (clareados e não clareados) e protocolo restaurador (sem tratamento, ascorbato de sódio 10% (10AS), ascorbato de sódio (35AS) e estratégia de condicionamento total de dois passos (ER) ou estratégia autocondicionante de um passo (SE) com o sistema adesivo Scotchbond universal. Quatro sessões de clareamento foram realizadas empregando peróxido de hidrogênio a 35%. Os espécimes do grupo controle foram mantidos em umidade relativa a 37 °C. Imediatamente após os procedimentos de clareamento, as soluções antioxidantes selecionadas foram empregadas na dentina e os procedimentos restauradores foram realizados seguindo as estratégias ER ou SE. Após 24 h, os espécimes foram submetidos ao teste de resistência ao cisalhamento. Os dados (MPa) foram analisados pela ANOVA e teste de Tukey (?=0,05). Os menores valores de resistência ao cisalhamento foram encontrados para os espécimes clareados (8,54 MPa) comparados com aqueles não clareados (12,13 MPa) (p<0,05). A resistência de união dos grupos tratados com ascorbato de sódio foi maior que aqueles não tratados (p<0,05), independentemente da estratégia empregada. Grupos restaurados sem ascorbato de sódio demonstraram menores valores de resistência de união para ambas as estratégias adesivas ER (8,32 MPa) e SE (8,28 MPa) (p<0,05). O grupo tratado com ascorbato de sódio a 10% submetido à estratégia ER (10,14 MPa) foi similar ao não tratado (p>0,05). Pode ser concluído que a resistência de união da resina composta à dentina intracoronária foi afetada pelo protocolo restaurador e reduzida pelo clareamento.

Bonding Effectiveness of Universal Adhesive to Intracoronal Bleached Dentin Treated with Sodium Ascorbate.

This study evaluated the effect of restorative protocol with sodium ascorbate on the shear bond strength (SBS) of a universal adhesive to intracoronal bleached dentin. One hundred-and-twenty bovine dentin fragments were randomly divided into 12 groups (n=10), according to the bleaching procedure (unbleached and bleached) and restorative protocol (no treatment, 10% sodium ascorbate -10SA, 35% sodium ascorbate -35SA and two-step etch-and-rinse -ER or one-step self-etch -SE Scotchbond universal adhesive approaches). Four whitening sessions were performed using 35% hydrogen peroxide. The samples from control groups were kept in relative humidity at 37 °C. Immediately after bleaching procedures, the assigned antioxidant solution was applied on dentin and restorative procedures were performed following either the ER or the SE approach. After 24 h, the specimens were subjected to SBS test. Data (MPa) were analyzed by ANOVA and Tukey's test (?=0.05). Lower SBS values were found for bleached specimens (8.54 MPa) compared with those unbleached (12.13 MPa) (p<0.05). The bond strength of the sodium ascorbate-treated groups was higher than those untreated, regardless of the strategy employed (p<0.05). Groups restored without sodium ascorbate showed lower bond strength values for both ER (8.32 MPa) and SE (8.28 MPa) adhesive strategies. The group treated with 10SA submitted to ER approach (10.14 MPa) was similar to untreated groups (p>0.05). It may be concluded that bond strength of composite resin to intracoronal dentin was affected by restorative protocol and reduced by bleaching.

Rehabilitation of weakened premolars with a new polyfiber post and adhesive materials.

BACKGROUND: Polyfiber posts used inside the root canal can help to restore the fracture resistance of weakened premolars. AIM: To assess the fracture resistance of endodontically treated premolars restored with different techniques, including the new polyfiber post (Spirapost). MATERIALS AND METHODS: One hundred superior premolars were distributed into 10 groups (n = 10): Sound teeth (G1-positive control) and experimental (G2 to G10), which received MODP cavities and canal treatment. Groups were restored as follows: G2 - unrestored (negative control); G3 - microhybrid resin (MR); G4 - flowable resin (FR) + (MR); G5 - glass fiber post (Reforpost) + MR; G6 - Reforpost + FR + MR; G7 - polyethylene fiber (Ribbond) + MR; G8 - Ribbond + FR + MR; G9 - polyfiber post (Spirapost) + MR and G10 - Spirapost + FR + MR. After 24 h, the specimens were loaded until fracture. Data were analyzed by ANOVA and Tukey's test (P < 0.05). RESULTS: Premolars restored with Spirapost (G9 and G10) provided the highest fracture strength (P < 0.05), similar to sound teeth (G1), regardless of the composite resin. Intermediate values were achieved by G3, G4, G5, G6, G7, and G8, which were similar (P > 0.05) and different from the others (P < 0.05). Inferior values were found in G2 (P < 0.05). CONCLUSION: Fracture resistance of premolars with MODP cavities and endodontic access was recovered with the direct rehabilitation with Spirapost, regardless of the type of composite resin.

Effect of Nd:YAG (1064-nm) and Diode Laser (980-nm) EDTA Agitation on Root Dentin Ultrastructure Properties.

OBJECTIVE: The purpose of this study was to analyze the effects of agitation of 17% ethylenediaminetetraacetic acid (EDTA) with 1064 nm Nd:YAG and 980 nm diode laser on root dentin microhardness and superficial roughness (with confocal laser scanning microscopy [CLSM]). BACKGROUND DATA: Root canal irrigants are used in an attempt to minimize the negative effects of smear layer. MATERIALS AND METHODS: Twenty-five bovine roots were sectioned longitudinally and divided into five groups (n=10 each): (1) deionized water, (2) 17% EDTA, (3) 17% EDTA with 60 sec manual agitation, (4) 17% EDTA with 50 sec diode laser (2 W) agitation, and (5) 17% EDTA with 50 sec Nd:YAG (1.5 W) laser agitation. Microhardness and superficial roughness values were calculated before and after the procedures at the cervical, middle, and apical root thirds. Microhardness was statistically analyzed using two way ANOVA, paired t test, and Tukey's tests (α=0.05). Roughness was statistically analyzed using Kruskal-Wallis, paired t test, and Student-Newman-Keuls tests (α=0.05%). RESULTS: Statistically significant differences in microhardness and roughness were observed between the deionized water group and others. EDTA with 1064 nm Nd:YAG or 980 nm diode laser presented the lowest microhardness and the highest roughness values and was significantly different from EDTA with manual agitation and EDTA only (p<0.05). However, there were no differences in microhardness or dentin roughness between the root thirds (p>0.05). CLSM analysis showed that the control samples exhibited smoother surfaces than that of the EDTA groups. CONCLUSIONS: Nd:YAG 1064 nm and 980-nm diode laser EDTA agitation caused greater reduction in microhardness and increased roughness of root dentin than EDTA only or EDTA with manual agitation.

Influence of apical enlargement in cleaning of curved canals using negative pressure system.

This study aimed to evaluate, by scanning electron microscopy (SEM), the cleaning of canal walls with moderate curvature subjected to biomechanical preparation with different final diameters using apical negative pressure irrigation. Thirty-two mesiobuccal roots of molars were divided into 4 groups (n=8) according to the instrument's final diameter: GI: 30.02, GII: 35.02, GIII: 40.02 and GIV: 45.02. Irrigating procedure was performed at each change of instrument with 1% NaOCl using the Endovac system. Final irrigation was conducted with 17% EDTA for 5 min. The SEM photomicrographs were evaluated under 35× and 1000× magnification, by three calibrated examiners, in a double-blind design. Data were submitted to Kruskal-Wallis and Dunn's post hoc tests (α=0.05). Canals instrumented with 30.02 and 35.02 final diameters showed more debris, statistically different from the other groups (p<0.05). Comparing each root canal third, for the cervical and apical portions no statistically significant difference (p>0.05) was found among the four groups. Regarding the presence of smear layer, canals with 30.02 final diameter showed the highest scores, statistically different from the 45.02 group (p<0.05) and similar to the 35.02 and the 40.02 groups (p>0.05). Although none of the studied diameters completely removed debris and smear layer, it may be concluded that instrumentation with higher final diameters was more effective in cleaning the root canals with moderate curvature.

Ultra-thin porcelain laminates to restore esthetics of anterior teeth: case report

Introduction: The ultra-thin porcelain laminates provide the esthetic harmony to the smile compromised by the presence of diastema between maxillary incisors. Objective: To report the dental aesthetic recovery with ultra-thin porcelain laminates, so-called "contact lenses". Case report: Patient sought treatment reporting presence of diastema between the anterior teeth. After the clinical examination, impressions were made to obtain study models and diagnostic wax-up. Home bleaching was conducted using 10% carbamide peroxide for 21 days. Next, the mock-up with bisacrylic self-curing composite resin and the functional impression were conducted. For cementation, dental surfaces were etched with 37% phosphoric acid followed by applying the adhesive system. The resin cement was inserted within internal part of the contact lenses previously treated with hydrof luoric acid and silane, and the prosthetic samples were positioned over the labial surfaces of the anterior teeth. After light-curing, the finishing procedure was performed. Conclusion: Ultra-thin porcelain laminates (contact lenses) were viable, efficient, and conservative procedures for recovering dental esthetic, with no need of invasive procedures.

Impact of Intracoronal Dentin Treatment Prior to Bleaching on Bond Strength of Restorative Materials

Surface treatment of dentin before the bleaching procedure may affect its permeability and influence the bond strength of restorative materials. This study evaluated the influence of surface treatment before the bleaching on shear bond strength (SBT) of restorative materials to intracoronal dentin. Dentin slabs were subjected to surface treatment: no bleaching (control - CON), no surface treatment + bleaching (HP), 37% phosphoric acid + bleaching (PA) and Er:YAG laser + bleaching (L). After the bleaching procedure, specimens (n=10) were restored with: microhybrid composite resin (MH), flowable composite resin (F), and resin-modified glass-ionomer cement (RMGIC). The shear test was carried out. ANOVA and Tukey's test (α=0.05) showed significant difference for surface treatment and restorative materials (p<0.05). CON presented higher STB and was statistically different from HP (p<0.05). PA and L showed intermediate values and were statistically similar to CON and HP (p>0.05). STB for MH and F were higher than RMGIC (p<0.05), and did not differ from each other (p>0.05). The surface treatments with phosphoric acid and Er:YAG laser before the bleaching procedure provided shear bond strength at the same level of unbleached dentin and the composite resins presented superior bond strength to the intracoronal dentin.

O tratamento superficial da dentina previamente ao clareamento pode afetar a sua permeabilidade e influenciar a resistência de união de materiais restaurados. Este estudo avaliou a influência do tratamento superficial antes do clareamento na resistência ao cisalhamento (RC) de materiais restauradores à dentina intracoronária. Fragmentos de dentina foram submetidos ao tratamento de superfície: não clareadas (controle - CON), sem tratamento de superfície + clareamento (HP), ácido fosfórico 37% + clareamento (AF), e laser Er:YAG + clareamento (L). Após o procedimento clareador, os espécimes foram restaurados com (n=10): resina composta micro-híbrida (MH), resina composta fluida (F), e cimento de ionômero de vidro modificado por resina (CIVMR). O teste de cisalhamento foi realizado. ANOVA e teste de Tukey (α=0,05) mostraram diferença significante para tratamento superficial e material restaurador (p<0,05). O grupo controle apresentou maior resistência de união e foi estatisticamente diferente de HP (p<0,05). AF e L mostraram valores intermediários e foram similares ao CON e HP (p>0,05). A resistência de união para MH e F foi maior que CIVMR (p<0,05), e não diferiram entre si (p>0,05). O tratamento da superfície dentinária com ácido fosfórico e laser Er:YAG previamente ao clareamento promoveu resistência de união ao nível da dentina não clareada e a adesão à dentina intracoronária foi superior com as resinas compostas.

Influence of Apical Enlargement in Cleaning of Curved Canals Using Negative Pressure System

This study aimed to evaluate, by scanning electron microscopy (SEM), the cleaning of canal walls with moderate curvature subjected to biomechanical preparation with different final diameters using apical negative pressure irrigation. Thirty-two mesiobuccal roots of molars were divided into 4 groups (n=8) according to the instrument's final diameter: GI: 30.02, GII: 35.02, GIII: 40.02 and GIV: 45.02. Irrigating procedure was performed at each change of instrument with 1% NaOCl using the Endovac system. Final irrigation was conducted with 17% EDTA for 5 min. The SEM photomicrographs were evaluated under 35× and 1000× magnification, by three calibrated examiners, in a double-blind design. Data were submitted to Kruskal-Wallis and Dunn's post hoc tests (α=0.05). Canals instrumented with 30.02 and 35.02 final diameters showed more debris, statistically different from the other groups (p<0.05). Comparing each root canal third, for the cervical and apical portions no statistically significant difference (p>0.05) was found among the four groups. Regarding the presence of smear layer, canals with 30.02 final diameter showed the highest scores, statistically different from the 45.02 group (p<0.05) and similar to the 35.02 and the 40.02 groups (p>0.05). Although none of the studied diameters completely removed debris and smear layer, it may be concluded that instrumentation with higher final diameters was more effective in cleaning the root canals with moderate curvature.

Este estudo buscou avaliar, por meio de microscopia eletrônica de varredura (MEV), a limpeza das paredes de canais com curvatura moderada, submetidos ao preparo biomecânico com diferentes diâmetros finais utilizando-se irrigação por pressão apical negativa. Trinta e duas raízes mésio-vestibulares de molares foram divididas em 4 grupos (n=8) de acordo com o diâmetro final dos instrumentos: GI: 30.02, GII: 35.02, GIII: 40.02 e GIV: 45.02. O procedimento de irrigação foi realizado a cada troca de instrumento com NAOCl 1% utilizando o sistema EndoVac. A irrigação final foi conduzida com EDTA 17% por 5 min. As microfotografias de MEV foram avaliadas sob aumentos de 35× e 1000×, por três examinadores calibrados, em estudo duplo-cego. Os dados foram submetidos ao teste de Kruskal-Wallis e pós-teste de Dunn (=0,05). Os canais instrumentados com diâmetros finais de 30.02 e 35.02 demonstraram mais debris, estatisticamente diferente dos demais grupos (p<0,05). Comparando-se cada terço do canal radicular, para as porções cervical e apical não foi encontrada diferença estatisticamente significante (p>0,05) entre os quatro grupos. Com relação à presença de smear layer, canais com diâmetro final de 30.02 demonstraram os maiores scores, estatisticamente diferente do grupo 45.02 (p<0,05) e similar aos grupos 35.02 e 40.02 (p>0,05). Apesar de nenhum dos diâmetros estudados ter removido completamente os debris e a smear layer, pode ser concluído que a instrumentação com diâmetros finais maiores foi mais efetiva na limpeza dos canais radiculares com curvatura moderada.

Effect of light sources on the bond strength of resin material to thin-walled roots.

The aim of this study was to evaluate the bond strength to the dentin of an adhesive material used for root reinforcement light activated with different sources. Roots were divided into 4 groups (n=15) according to the light source used to activate the resin reinforcement: GI, non-weakened roots (control); GII, halogen light (H) 600 mW/cm²; GIII, LED 800 mW/cm² and GIV, LED 1500 mW/cm². The reinforcement was done with adhesive, composite resin and fiberglass posts. After 24 h, the specimens were sectioned and the first slice of each post region was used in the push out test in a universal testing machine with a crosshead speed of 0.5 mm/min. Failure modes of the debonded specimens were examined. Data (MPa) were analyzed by ANOVA and Holm-Sidak test (α=0.05). The second slice from each region was analyzed by scanning electron microscopy (SEM). LED-1500 (4.69 ± 1.74) provided bond strength similar to the control group (5.05 ± 2.63) and statistically different from H-600 (1.96 ± 0.94) and LED-800 (2.75 ± 1.90), which were similar to each other (p<0.05). Cervical (4.16 ± 2.32) and middle (4.43 ± 2.32) regions showed higher bond strength than the apical (2.25 ± 1.50) (p<0.05). There was a prevalence of adhesive failures in H-600 and LED-800 and cohesive failures in LED-1500. SEM showed the formation of long, numerous and fine tags. It was concluded that LED-1500 provided higher bond strength of resin reinforcement to the dentin.

Impact of chemical agents for surface treatments on microhardness and flexural strength of root dentin.

This study assessed the cross-sectional Knoop microhardness and flexural strength of root dentin exposed to different surface treatments with chemical agents after biomechanical preparation. Root canals from human canines were biomechanically treated and divided into eight groups (n=10) to receive one of the following dentin treatments: I. Deionized water (control); II. 5.25% Sodium hypochlorite (NaOCl); III. NaOCl + 10% Sodium ascorbate (SA); IV. SA; V. 2% Chlorhexidine gel (CHX); VI. 37% Phosphoric acid gel (PA) + CHX; VII. PA; and VIII. PA + NaOCl. The roots were sectioned to obtain specimens that were evaluated for cross-sectional Knoop microhardness and flexural strength using a three-point bending test. ANOVA and Tukey's test were performed. The microhardness in the control group was significantly higher (p < 0.05) than in the groups exposed to chemical agents, which in turn were statistically similar (p > 0.05) to each other. Regarding flexural strength, PA+NaOCl provided statistical higher values than PA+CHX and CHX. However, there was no significant difference between the control group and those groups subjected to surface treatment (p > 0.05). Dentin microhardness was reduced after exposure to NaOCl, CHX, PA, SA and their associations and the flexural strength of radicular dentin was not affected by the chemical agents.

Bond strength of restorative material to dentin submitted to bleaching and Er:YAG laser post-treatment.

OBJECTIVE: The purpose of this study was to assess the bond strength of a restorative material to bleached dentin, pretreated with Er:YAG laser. BACKGROUND DATA: Laser irradiation for dental surface treatment may increase the bond strength of restorative material to tooth surface. There are no reports of using Er:YAG laser on dentin bleached with 35% hydrogen peroxide. METHODS: Forty maxillary canines were sectioned, resulting in 80 fragments (5×5 mm) of intracoronary dentin that were divided into eight groups (n=10) according to the dental bleaching (present or not), surface conditioning (with or without laser) and the post-bleaching time to perform restoration (immediately or 7 days). The bleached specimens received two applications of 38% hydrogen peroxide. Er:YAG laser was applied for 20 sec with 400 mJ/15 Hz. Restorative procedure was performed using phosphoric acid, an adhesive system, and resin using a split Teflon matrix. The specimens were submitted to shear bond strength test and the data (MPa) were analyzed by ANOVA and Tukey's test (α=0.05). RESULTS: There were significant differences among the three factors (p<0.05). The highest values were obtained for unbleached specimens compared with bleached, for those treated with laser compared with those only conditioned with acid, and for those restored after 7 days compared with those having immediate restoration. In the interaction of factors, the bleached specimens treated with laser and restored immediately were statistically similar (p>0.05) to those bleached and restored after 7 days. CONCLUSIONS: Er:YAG laser can restore the bond strength of the dentin/restorative material interface even if the restoration is performed immediately after bleaching.

Effect of Light Sources on the Bond Strength of Resin Material to Thin-walled Roots

The aim of this study was to evaluate the bond strength to the dentin of an adhesive material used for root reinforcement light activated with different sources. Roots were divided into 4 groups (n=15) according to the light source used to activate the resin reinforcement: GI, non-weakened roots (control); GII, halogen light (H) 600 mW/cm2; GIII, LED 800 mW/cm2 and GIV, LED 1500 mW/cm2. The reinforcement was done with adhesive, composite resin and fiberglass posts. After 24 h, the specimens were sectioned and the first slice of each post region was used in the push out test in a universal testing machine with a crosshead speed of 0.5 mm/min. Failure modes of the debonded specimens were examined. Data (MPa) were analyzed by ANOVA and Holm-Sidak test (=0.05). The second slice from each region was analyzed by scanning electron microscopy (SEM). LED-1500 (4.69 ± 1.74) provided bond strength similar to the control group (5.05 ± 2.63) and statistically different from H-600 (1.96 ± 0.94) and LED-800 (2.75 ± 1.90), which were similar to each other (p<0.05). Cervical (4.16 ± 2.32) and middle (4.43 ± 2.32) regions showed higher bond strength than the apical (2.25 ± 1.50) (p<0.05). There was a prevalence of adhesive failures in H-600 and LED-800 and cohesive failures in LED-1500. SEM showed the formation of long, numerous and fine tags. It was concluded that LED-1500 provided higher bond strength of resin reinforcement to the dentin.

O objetivo deste estudo foi avaliar a resistência de união à dentina de uma resina utilizada para reforço de raiz, ativada com diferentes fontes de luz. De acordo com a fonte de luz utilizada as raízes foram divididas em 4 grupos (n = 15): GI, raízes não fragilizadas (controle); GII, luz halógena (H) 600 mW/cm2; GIII, LED 800 mW/cm2 e GIV, LED 1500 mW/cm2. O reforço foi feito com adesivo, resina composta e pino de fibra de vidro. Após 24 h, os espécimes foram seccionados e o primeiro slice de cada região utilizado para o teste de união push out, na máquina de ensaios universais com 0,5 mm/min, e o tipo da falha avaliada. Os dados obtidos (MPa) foram analisados utilizando os testes de ANOVA e Holm-Sidak (=0.05). O segundo slice de cada região foi analisado por microscopia eletrônica de varredura (MEV). O LED-1500 (4.69 ± 1.74) proporcionou resistência a união similar ao controle (5.05 ± 2.63) e estatisticamente diferente do H-600 (1.96 ± 0.94) e LED-800 (2.75 ± 1.90), que são similares entre si (p<0.05). As regiões cervical (4.16 ± 2.32) e média (4.43 ± 2.32) apresentaram alta resistência à união quando comparadas à região apical (2.25 ± 1.50) (p<0.05). Houve uma predominância de falhas adesivas com as fontes de luzes H-600 e LED-800 e coesivas com o LED-1500. A análise em MEV demonstrou a formação de longos tags resinosos. Desta forma, pode-se concluir que o LED-1500 proporcionou maior resistência à resina utilizada para o reforço da dentina radicular.

Impact of intracoronal dentin treatment prior to bleaching on bond strength of restorative materials.

Surface treatment of dentin before the bleaching procedure may affect its permeability and influence the bond strength of restorative materials. This study evaluated the influence of surface treatment before the bleaching on shear bond strength (SBT) of restorative materials to intracoronal dentin. Dentin slabs were subjected to surface treatment: no bleaching (control - CON), no surface treatment + bleaching (HP), 37% phosphoric acid + bleaching (PA) and Er:YAG laser + bleaching (L). After the bleaching procedure, specimens (n=10) were restored with: microhybrid composite resin (MH), flowable composite resin (F), and resin-modified glass-ionomer cement (RMGIC). The shear test was carried out. ANOVA and Tukey's test (α=0.05) showed significant difference for surface treatment and restorative materials (p<0.05). CON presented higher STB and was statistically different from HP (p<0.05). PA and L showed intermediate values and were statistically similar to CON and HP (p>0.05). STB for MH and F were higher than RMGIC (p<0.05), and did not differ from each other (p>0.05). The surface treatments with phosphoric acid and Er:YAG laser before the bleaching procedure provided shear bond strength at the same level of unbleached dentin and the composite resins presented superior bond strength to the intracoronal dentin.

Tensile Strength of Glass Fiber Posts Submitted to Different Surface Treatments

The aim of this in vitro study was to evaluate the tensile strength of glass fiber posts submitted to different surface treatments. Forty-eight maxillary canines had their crowns sectioned and root canals endodontically treated. The roots were embedded in acrylic resin and distributed into 3 groups according to the surface treatment: Group I: the posts were treated with silane agent for 30 s and adhesive; Group II: the posts were cleaned with alcohol before treatment with silane agent and adhesive; Group III: the posts were submitted to conditioning with 37% phosphoric acid for 30 s before treatment with silane agent and adhesive. Each group was divided into 2 subgroups for adhesive polymerization or not before insertion into the canal: A - adhesive was not light cured and B - adhesive was light cured. All posts were cemented with Panavia F and the samples were subjected to tensile strength test in a universal testing machine at crosshead speed of 1 mm/min. Data were submitted to one-way ANOVA and Tukey's test at 5% significance level. There was statistically significant difference (p<0.01) only between group GIII-B and groups GI-A and GI-B. No significant difference was found among the other groups (p>0.05). It was concluded that the products used for cleaning the posts influenced the retention regardless of adhesive light curing.

O objetivo deste estudo in vitro foi avaliar a resistência à tração de pinos de fibra de vidro submetidos a diferentes tratamentos de superfície. Quarenta e oito caninos superiores tiveram suas coroas seccionadas e as raízes tratadas endodonticamente. As raízes foram incluídas em resina acrílica e distribuídas em 3 grupos de acordo com o tratamento de superfície aplicado aos pinos: Grupo I: os pinos receberam agente silano por 30 s e adesivo; Grupo II: os pinos foram limpos com álcool e então receberam o agente silano e adesivo; Grupo III: os pinos foram submetidos ao condicionamento com ácido fosfórico a 37% por 30 s, seguido de agente silano e adesivo. Cada grupo foi dividido em 2 subgrupos de acordo com fotoativação do adesivo antes da inserção do pino no interior do canal: A – adesivo não foi fotoativado, B: o adesivo foi fotoativado. Todos os pinos foram cimentados com Panavia F e as amostras foram submetidas a teste de tração utilizando máquina universal de ensaios, com velocidade de 1 mm/min. Os dados obtidos foram submetidos à ANOVA a um critério e ao teste de Tukey com nível de significância de 5%. Houve diferença estatisticamente significante (p<0,01) entre o grupo GIII-B e os grupos GI-A e GI-B. Os demais grupos não apresentaram diferenças significantes entre si (p>0,05). Pode-se concluir que as substâncias utilizadas para a limpeza dos pinos interferiram em sua retenção, independente da fotopolimerização do adesivo.

Tensile strength of glass fiber posts submitted to different surface treatments.

The aim of this in vitro study was to evaluate the tensile strength of glass fiber posts submitted to different surface treatments. Forty-eight maxillary canines had their crowns sectioned and root canals endodontically treated. The roots were embedded in acrylic resin and distributed into 3 groups according to the surface treatment: Group I: the posts were treated with silane agent for 30 s and adhesive; Group II: the posts were cleaned with alcohol before treatment with silane agent and adhesive; Group III: the posts were submitted to conditioning with 37% phosphoric acid for 30 s before treatment with silane agent and adhesive. Each group was divided into 2 subgroups for adhesive polymerization or not before insertion into the canal: A - adhesive was not light cured and B - adhesive was light cured. All posts were cemented with Panavia F and the samples were subjected to tensile strength test in a universal testing machine at crosshead speed of 1 mm/min. Data were submitted to one-way ANOVA and Tukey's test at 5% significance level. There was statistically significant difference (p<0.01) only between group GIII-B and groups GI-A and GI-B. No significant difference was found among the other groups (p>0.05). It was concluded that the products used for cleaning the posts influenced the retention regardless of adhesive light curing.